Maxxam™ X MX5200-8054 FR NC001
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2X3aK7_MaxxamXMX52008054FRNC001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, flame retardant and low blooming |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.6 - 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 200 | % | ASTM D638 |
| Flexural Modulus 3 | 1300 | MPa | ASTM D790 |
| Flexural Strength 4 | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | V-0 | Internal method | |
| Glow Wire Flammability Index | 875 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 85 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30 - 60 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Verolloy A2703 | PlastxWorld Inc. | ABS+Nylon | Verolloy |
| Xuchuan 1065G/B-5009 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| FHR Polypropylene P5M6K-048 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| MACOMASS PP MM-PP HI 21 (10% Talc) | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| Durethan® BKV 15 H2.0 DUS008 901510 | LANXESS Corporation | Nylon 6 | Durethan® |