Braskem PE ML3600S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2U5VQH_Braskem-PE-ML3600S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The resin ML3600S is a Linear Low Density Polyethylene, 1-hexene copolymer, developed for rotomolding. It presents an adequate balance of processability and mechanical properties, with good resistance to environmental stress cracking. Applications: Water tanks, tanks, parts for the automotive and agricultural segments. Processing Conditions: This resin is recommended to rotational molding under conditions comparable to polyethylene resins with similar melt index and density range. Oven Temperature Range: 260 to 350 °C. P.I.A.T:210 to 240°C. Additives: Weathering resistance UV8 and antioxidants. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.933 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.7 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1 | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | 250 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 19.0 | MPa | ASTM D638 |
| Fracture, molding | 29.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 14 | % | ASTM D638 |
| Fracture, molding | > 1000 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 770 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | ARM | ||
| -40°C, 3.17mm, rotational molding | 55 | J | ARM |
| -40°C, 6.34mm, rotational molding | 115 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, molded | 60.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, molded | 42.0 | °C | ASTM D648 |
| Peak Melting Temperature | 127 | °C | ASTM D3418 |
| Injection instructions |
|---|
| Oven Temperature Range: 260 to 350 °C. |
| Note Message | |
|---|---|
| 1 . | 0.3mm notched-plaques |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PP 1370 | Premix Oy | TPO | PRE-ELEC® |
| Xuchuan XAC-75 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Hanwha Total PP WH72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hyundai EP Breathable AT910/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| Braskem PE HS4506 | Braskem | HDPE | Braskem PE |