Lutene® H XL1800
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GnZB1W_Lutene-H-XL1800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUTENE-H XL1800 is a optimum material for under-floor heating and drinking water Pipe by RAM type extrusion. It is a excellent product with long-term internal pressure creep propperty and crosslinking property, mechanical properties. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 2.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 8760 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield 1 | 2.45 | MPa | ASTM D638 |
| Fracture | 3.43 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 800 | % | ASTM D638 |
| Flexural Modulus 3 | 981 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 123 | °C | ASTM D1525 4 |
| Melting Temperature | 133 | °C | DSC |
| Additional Information |
|---|
| Molecular Weight Distribution, LG Method, GPC: Narrow |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE FM-2163N | Teknor Apex Company | TPE | Sarlink® TPE |
| Sekisui PVC TG-H500 | Sekisui (Hong Kong) Limited | PVC, Unspecified | Sekisui PVC |
| Wondel® P PM8 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| EASYPOXY® K-230 | Cytec Industries Inc. | Epoxy | EASYPOXY® |
| Hyundai EP PA6 LS180 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |