SCHULAMID® 6 MV HI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2NDRs5_SCHULAMID-6-MV-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Higher impact Polyamide 6 - standard grade |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 2.3 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 110 | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2200 | 800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 60.0 | 35.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.2 | 20 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 50 | > 100 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 16 | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 140 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 215 | -- | °C | ISO 306/A50 |
| -- | 175 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 650 | °C | |
| 3.00 mm | -- | 650 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Polyurethane F-32 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Borealis PP EE002AE | Borealis AG | PP, Unspecified | Borealis PP |
| ELASTOSIL® AUX MOULD RELEASE AGENT 32 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| Latistat 52/7-02 MI/30 | LATI S.p.A. | PP Homopolymer | Latistat |
| Braskem PE HT5303 | Braskem | HDPE | Braskem PE |