Trexprene® A88SCI-HF
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2KwUHQ_Trexprene-A88SCI-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A88SCI-HF is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV) which contains a lubricant/slip package for lower co-efficient of friction and anti-wear properties versus normal TPV's. This compound is formulated in pre-color form primarily for under-hood or interior applications. This material can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.870 to 0.930 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 82 to 90 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wear Resistance 1 | No appreciable loss of grain, texture or color | ASTM D3844 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging - Dry Fog | 79 | % | SAE J1756 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Color Fastness | |||
| to Burnt Gas, AATCC Rating : 60°C 2 | > 4.00 | ||
| to Burnt Gas, Change in Color : 60°C 3 | Delta E < 3 | ||
| to Burnt Gas, Yellowness Index : 60°C 4 | < 2.00 | YI | |
| to Light 5 | Delta E < 3 | ||
| Linting 6 | Rating less than 2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 7(100% Strain) | 5.90 | MPa | ISO 37 |
| Tensile Stress - Across Flow 8(Break) | 10.2 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 9(Break) | 670 | % | ISO 37 |
| Tear Strength - Across Flow 10 | 42 | kN/m | ISO 34-1 |
| Compression Set | |||
| 70°C, 22 hr | 47 | % | ASTM D395B |
| 70°C, 22 hr 11 | 47 | % | ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -51.0 | °C | ASTM D746 |
| Type B | -51.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 32 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | 1000 cycles CS10 Wheel (500 g load) |
| 2 . | ISO 105-G02, AATCC TM 23, 168 h |
| 3 . | ISO 105-G02, AATCC TM 23, 168 h |
| 4 . | ISO 105-G02, AATCC TM 23, 168 h |
| 5 . | SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
| 6 . | LP-463KB-37-01, Method A |
| 7 . | Type 1, 500 mm/min |
| 8 . | Type 1, 500 mm/min |
| 9 . | Type 1, 500 mm/min |
| 10 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 11 . | Type A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1600 L | RTP Company | PAS | RTP |
| THERMOLAST® K TC5CSN (Series: CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Tritan™ MX811 | Eastman Chemical Company | Copolyester | Tritan™ |
| Aropol™ L 2450 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Hylon® N2230HL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |