HiFill® PEEK GF10
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2H5C1k_HiFill-PEEK-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PEEK GF10 is a Polyetheretherketone (PEEK) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 5310 | MPa | ASTM D790 |
| Flexural Strength | 153 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 249 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 360 to 388 | °C | |
| Middle Temperature | 360 to 388 | °C | |
| Front Temperature | 360 to 388 | °C | |
| Processing (Melt) Temp | 360 to 382 | °C | |
| Mold Temperature | 177 to 218 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 5002 | Colorite Polymers | PVC, Unspecified | Unichem |
| Adell Polyamide AT-14 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Borealis FR4847 | Borealis AG | PE, Unspecified | Borealis |
| Andur 90 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| C-Clear™ K7030 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | C-Clear™ |