Generic PP, Unspecified - Glass Fiber, Long
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 28avOZ_Generic-PP-Unspecified---Glass-Fiber-Long.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass Fiber, Long This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.180 - 1.35 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.020 - 0.31 | % | ASTM D955 |
| Transverse flow : 23°C | 0.29 - 0.61 | % | ASTM D955 |
| 23°C | 0.080 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 105 - 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 560 - 10900 | MPa | ASTM D638 |
| 23°C | 4280 - 14000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 73.5 - 148 | MPa | ASTM D638 |
| Yield, 23°C | 96.1 - 122 | MPa | ISO 527-2 |
| Fracture, 23°C | 97.0 - 131 | MPa | ASTM D638 |
| Fracture, 23°C | 82.6 - 151 | MPa | ISO 527-2 |
| 23°C | 5.00 - 126 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.8 - 3.0 | % | ASTM D638 |
| Fracture, 23°C | 1.7 - 2.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3330 - 9450 | MPa | ASTM D790 |
| 23°C | 3810 - 11400 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 150 - 190 | MPa | ASTM D790 |
| 23°C | 108 - 288 | MPa | ISO 178 |
| Coefficient of Friction | 0.34 - 0.52 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 - 33 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 39 - 75 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 150 - 300 | J/m | ASTM D256 |
| 23°C | 17 - 29 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 740 - 770 | J/m | ASTM D256 |
| 23°C | 44 - 66 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 1.50 - 16.3 | J | ASTM D3763 |
| 23°C | 5.59 - 13.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 158 - 165 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 162 - 164 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 149 - 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 155 - 161 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 122 - 138 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 145 - 166 | °C | ISO 306 |
| Melting Temperature | 165 - 166 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 2.2E-5 - 6.8E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.8E-5 - 4.7E-5 | cm/cm/°C | ASTM E831 |
| Flow | 3.3E-5 - 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.5E-5 - 8.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.6E-5 - 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 95.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 225 - 260 | °C | |
| Middle Temperature | 224 - 265 | °C | |
| Front Temperature | 244 - 275 | °C | |
| Nozzle Temperature | 240 - 285 | °C | |
| Processing (Melt) Temp | 234 - 275 | °C | |
| Mold Temperature | 48.8 - 55.0 | °C | |
| Injection Pressure | 45.0 - 90.0 | MPa | |
| Holding Pressure | 59.6 - 60.0 | MPa | |
| Back Pressure | 0.250 - 1.52 | MPa | |
| Screw Speed | 45 - 90 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Glass Fiber, LongThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3571EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| Propafoil™ RVG120 | Innovia Films Ltd. | PP Alloy | Propafoil™ |
| Sylvin 5132-90UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DIOSHY® TPO F963D-OS | DIOSHY Co.,Ltd. | TPO (POE) | DIOSHY® |
| Jampilen EP440L | Jam Polypropylene Company | PP Copolymer | Jampilen |