INEOS LLDPE LL6208AF
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ngkaY_INEOS-LLDPE-LL6208AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6208AF has been developed for use in rich blends in heavy duty sacks, liners and other thin film applications requiring excellent mechanical performance. This grade is also recommended for artificial grass applications. LL6208AF is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL6208AF. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 38 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% secant, TD : 38 µm, blown film | 240 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 38 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : 38 µm, blown film | 60.0 | MPa | ISO 527-3 |
| TD : 38 µm, blown film | 44.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 38 µm, blown film | 750 | % | ISO 527-3 |
| TD : Broken, 38 µm, blown film | 900 | % | ISO 527-3 |
| Dart Drop Impact (38 µm, Blown Film) | 250 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38.0 µm | 96.1 | kN/m | ASTM D1922 |
| TD : 38.0 µm | 213.8 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 109 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 61 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RenPIM® VG 5234 Polyol/ 5234 Isocyanate | Huntsman Advanced Materials | PUR, Unspecified | RenPIM® |
| T-Blend® 4404N-PE | TSRC Corporation | TPE | T-Blend® |
| ALTECH® PA6 A 2030/209 GF30 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| ENFLEX S3185AE | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Lucky Enpla LGF1100 | Lucky Enpla Co LTD | PC | Lucky Enpla |