Epocast 1652-A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wiQ1uG_Epocast-1652-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast ® 1652-A/B epoxy syntactic is a low-density system with good elevated temperature performance after a room-temperature cure. The epoxy syntactic is suitable for core filling metal skins, adding stiffness and strength to fabricated parts such as helicopter rotor blades, core splicing, and strengthening radii and corners of reinforced plastic structures. Epocast ® 1652-A/B epoxy syntactic is qualified to Grumman GM 4006, Gulfstream GMS 4005 and Sikorsky 9587, Type 2. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.798 | g/cm³ | ASTM D1622 |
| -- 1 | 0.998 | g/cm³ | ASTM D1622 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 25°C 2 | 62.1 | MPa | ASTM D695 |
| 2% strain, 177°C | 4.48 | MPa | ASTM D695 |
| 2% strain, 25°C | 55.2 | MPa | ASTM D695 |
| 2% strain, 82°C | 27.6 | MPa | ASTM D695 |
| 2% strain, -55°C | 65.5 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 12 | ||
| Shelf Life (25°C) | 52 | wk | |
| Thermoset Mix Viscosity 3(25°C) | 500 | cP | ASTM D2196 |
| Gel Time - System (25°C) 4 | 30.0 - 60.0 | min | ASTM D2471 |
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C | Semi-paste | ASTM D2196 | |
| Resin : 25°C | Paste | ASTM D2196 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 7.0 | day | |
| Tensile Lap Shear - Etched AL/AL (25°C) | 4.83 | MPa | ASTM D1002 |
| CURE SCHEDULE: Seven days at 77°F (25°C), or gel at 77°F (25°C) followed by 2-3 hours at 150°F (66°C ). |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Break |
| 3 . | Hardener |
| 4 . | 100 gms |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 6145N | Teknor Apex Company | TPV | Sarlink® TPV |
| Witcom POM-C 2008/325 Blue | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Hifax TRC 779P E 1750 | LyondellBasell Industries | PP Copolymer | Hifax |
| Karina BLACK PVC COMPOUD 852D48/ 1-J-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polygen SC75D-BK | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |