MARPOL® LDF 701-B
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1f9CDp_MARPOL-LDF-701-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Recommended Applications Bread bags, co-extrusion films, collation shrink, diaper backsheets, foams, high performance collation, shrink, hygiene packaging, label film, laminating film and overwrap paper and film. Description MARPOL® LDF 701-B is a homopolymer film resin with great clarity and stiffness. Film made from this resin may be used in overwrap applications and in push-through type packaging equipment. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 234 | MPa | |
| 1% Secant, TD | 290 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.0 | MPa | |
| TD : Yield | 11.7 | MPa | |
| MD : Break | 25.5 | MPa | |
| TD : Break | 22.1 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 130 | % | |
| TD : Break | 540 | % | |
| Dart Drop Impact | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 510 | g | |
| TD | 140 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Peak Melting Temperature | 113 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 57 | ASTM D2457 | |
| Haze | 9.6 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2932-67 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| DENKA POVAL H-24 | Denka Company Limited | PVOH | DENKA POVAL |
| KOPLA PA66 KDG1060 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Hostacom DG 154 2 C13084 | LyondellBasell Industries | PP Copolymer | Hostacom |
| SIBUR Synthetic Rubber NBR 1855 | SIBUR | NBR | SIBUR Synthetic Rubber |