PRL TP-FR-G7.5
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1ZWTZe_PRL-TP-FR-G7-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-FR-G7.5 is a Polybutylene Terephthalate (PBT) product filled with 7.5% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 10 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 82.7 | MPa | |
| Break, 3.18 mm | 82.7 | MPa | |
| Flexural Modulus (3.18 mm) | 3450 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 121 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 199 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 149 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226F5RY01 | SAX Polymers | Nylon 66 | SAXAMID™ |
| AgroResin™ AgroResin™ | Grenidea Technologies Pte Ltd | Biodeg Polymers | AgroResin™ |
| Mafill® HT 4202 | Ravago Group | PP Homopolymer | Mafill® |
| Celanex® 3201 | Celanese Corporation | PBT | Celanex® |
| STYRON™ 2678 MED | Trinseo | PS (GPPS) | STYRON™ |