Silamid® SV15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Roonamid a.s. |
| Trademark: | Silamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1YQfG6_Silamid-SV15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA6 reinforced with 15 % short glass fibres, natural and black colour and in colourly shades according to customer´s requests, optimal flowing properties, technical mouldings with increased claims to rigidity, strength, shape stability, eventually electroinsulating properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow | 1.3 | 1.3 | % | |
| Flow | 0.30 | 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 0.90 | 0.90 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6000 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 75.0 | MPa | ISO 527-2 |
| Flexural Modulus | 4500 | 2200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | -- | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | -- | 0.14 | IEC 60250 | |
| Arc Resistance | 95.0 | -- | sec | ASTM D495 |
| Comparative Tracking Index (Solution A) | -- | 400 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature | 650 | 650 | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130A93 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| VESTODUR® X4877 | Evonik Industries AG | PBT | VESTODUR® |
| Zytel® 105F BK010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| GAPEX® RPP20EU65GY | Ferro Corporation | PP, Unspecified | GAPEX® |
| Karina COMP. PVC CRYSTAL -E 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |