PRIME TPO J-5900
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | PRIME TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fSLRC8_PRIME-TPO-J-5900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRIME TPO J-5900 is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in Asia Pacific, Europe, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 17.5 | MPa | |
| Break | 21.5 | MPa | |
| Tensile Strain (Break) | < 500 | % | ISO 527-2 |
| Flexural Modulus | 420 | MPa | ISO 178 |
| Flexural Stress | 17.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 80 | µm | |
| Tensile Modulus | JIS Z1702 | ||
| MD : 80 µm | 430 | MPa | |
| TD : 80 µm | 430 | MPa | |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 80 µm | 40.0 | MPa | |
| TD : Break, 80 µm | 40.0 | MPa | |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 80 µm | < 500 | % | |
| TD : Break, 80 µm | < 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 15 | kJ/m² | ISO 180 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | JIS K7105 | ||
| 80.0 µm 1 | 0.60 | % | |
| 80.0 µm 2 | 4.0 | % |
| Note Message | |
|---|---|
| 1 . | Internal |
| 2 . | All |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4560 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Rainmaker Polypropylene MCCPTL20 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| TOTAL Polystyrene Compound 820 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Weifang Kingdom CPE135A | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| Next PC CX-02GY | Next Polymers Ltd. | PC | Next PC |