LNP™ STAT-KON™ DX09303C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1GKEgB_LNP-STAT-KON-DX09303C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON DX09303C is carbon fiber filled polycarbonate composite with high modulus, good flow ability, and high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 47.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.050 to 0.15 | % | |
| Across Flow : 3.20 mm | 0.10 to 0.25 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 20100 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 161 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 18000 | MPa | ASTM D790 |
| Flexural Strength | 246 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 82 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 600 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 125 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 4.4E-6 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 to 5.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 280 to 320 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-951U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Tecodur® PB70 BK001 MC | Eurotec Engineering Plastics | PBT | Tecodur® |
| Sylvin 8409-80 Natural | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| CALIBRE™ IM 401-18 | Trinseo | PC | CALIBRE™ |
| LNP™ LUBRICOMP™ RBG16I compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |