EQUATE PE EGDA-6888
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | EQUATE Petrochemical Company KSCC |
| Trademark: | EQUATE PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OhQECt_EQUATE-PE-EGDA-6888.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EGDA-6888 is a high molecular weight, high density polyethylene copolymer that has been designed specifically for tubular film extrusion. Its broad molecular weight distribution and density have been optimized to give excellent bubble stability at high extrusion rates with high film strength and rigidity. The combination of high strength and excellent drawdownability makes EGDA-6888 ideal for down gauging in many applications. Tubular films produced from EGDA-6888 are recommended for high strength grocery sacks, shopping bags, produce bags and high quality thin films for multiwall sack liners and replacements for thin paper products. Films are nearly gel-free and have excellent treatability. They are ideally suited for printing of high quality graphics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Bulk Density | 560 | kg/m³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 15 µm, Blown Film | 1220 | MPa | |
| 1% Secant, TD : 15 µm, Blown Film | 1470 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 15 µm, Blown Film | 60.0 | MPa | |
| TD : Break, 15 µm, Blown Film | 57.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm, Blown Film | 380 | % | |
| TD : Break, 15 µm, Blown Film | 550 | % | |
| Dart Drop Impact (15 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15.0 µm | 70.0 | kN/m | |
| TD : 15.0 µm | 150.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 131 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 215 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 3722 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Ferro PP NPP00GC24NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| KumhoSunny PA/PPE HAP8720G | Shanghai KumhoSunny Plastics Co., Ltd. | Nylon+PPE | KumhoSunny PA/PPE |
| Leona™ 91G55 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Sylvin 802-90 GREEN 358 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |