Clariant PBT PBT-1100G15
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 1EzSSW_Clariant-PBT-PBT-1100G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant PBT PBT-1100G15 is a polybutene terephthalate (PBT) material, which contains a 15% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main features of Clariant PBT PBT-1100G15 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 78 | ASTM D785 | |
| Class r | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 4830 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 221 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 202 | °C | ASTM D648 |
| Melting Temperature | 220 - 225 | °C | |
| CLTE - Flow | 5.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.794 mm | HB | UL 94 | |
| 1.59 mm | HB | UL 94 | |
| 3.18 mm | HB | UL 94 | |
| 6.35 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 - 274 | °C | |
| Middle Temperature | 232 - 274 | °C | |
| Front Temperature | 232 - 274 | °C | |
| Processing (Melt) Temp | 232 - 246 | °C | |
| Melt Temperature (Aim) | 241 | °C | |
| Mold Temperature | 65.6 - 82.2 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 80 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. pressure phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 165°FScrew Speed Target: 50 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4598 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SPESIN® KP270GR | Kolon Plastics, Inc. | PBT | SPESIN® |
| Sunny® PA6 HF230 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 6 | Sunny® |
| BMC HT12-1024 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Plenco 01501 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |