| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0mWG5w_Lupolen-2421-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupolen 2421 F is an additivated, low density polyethylene. It contains an antioxidant and is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 11.0 | MPa | ISO 527-2 |
| Coefficient of Friction | > 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 25 to 100 µm | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, Blown Film | 26.0 | MPa | |
| TD : 50 µm, Blown Film | 24.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 300 | % | |
| TD : Break, 50 µm, Blown Film | 600 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 150 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 50.0 µm, Blown Film | > 40 | ||
| 60°, 50.0 µm, Blown Film | > 90 | ||
| Haze (50.0 µm, Blown Film) | < 8.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Failure Energy 1(50.0 µm) | 5.50 | DIN 53372 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive SE900-5 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| XANTAR® C MC 3440 | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |
| Plexiglas® Resist zk6BR | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Diakon® CTG625 | Lucite International Holland BV | Acrylic (PMMA) | Diakon® |
| PPR PA6605HS | Premier Plastic Resins, Inc. | Nylon 66 | PPR |