Wanthane® WHT-7185

Category:	PC+TPU , Polycarbonate + TPU
Manufacturer:	Wanhua Chemical Group Co., Ltd.
Trademark:	Wanthane®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3qeuTL_Wanthane-WHT-7185.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

WHT-7185 is polycarbonate-based TPU, supplied in form of transparent, translucent, colorless or slightly yellowish pellets with the characteristics such as:

Higher Mechanical Strength

As good hydrolytic stability as polyether-based TPU

Better chemical resistance than other polyester-based TPUs

Better weather resistance such as heat and fungus resistance than common polyester-based TPUs WHT-7180 is polycarbonate-based TPU, supplied in form of transparent, translucent, colorless or slightly yellowish pellets with the characteristics such as:

Higher Mechanical Strength

As good hydrolytic stability as polyether-based TPU

Better chemical resistance than other polyester-based TPUs

Better weather resistance such as heat and fungus resistance than common polyester-based TPUs

Applications:
Wire & Cable, Film & Sheet, Hose & Tube, Animal Tag, Fire Hose, Sports Equipments etc.

General Information
Features	Fungus Resistant Good Chemical Resistance Good Strength Hydrolytically Stable Medium Heat Resistance
Uses	Film Hose Sheet Sporting Goods Tubing Wire & Cable Applications
Appearance	Colorless Translucent Transparent - Slight Yellow
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.22	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	85		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
100% Strain	8.00	MPa
300% Strain	23.0	MPa
Tensile Strength	35.0	MPa	ASTM D412
Tensile Elongation (Break)	350	%	ASTM D412
Tear Strength	100	kN/m	ASTM D624

Injection	Nominal Value	Unit
Drying Temperature	80.0 to 90.0	°C
Drying Time	3.0 to 4.0	hr
Rear Temperature	190	°C
Middle Temperature	195	°C
Front Temperature	200	°C
Nozzle Temperature	195	°C
Injection Pressure	80.0	MPa

Extrusion	Nominal Value	Unit
Drying Temperature	80.0 to 90.0	°C
Drying Time	3.0 to 4.0	hr
Cylinder Zone 1 Temp.	185	°C
Cylinder Zone 3 Temp.	190	°C
Cylinder Zone 5 Temp.	195	°C
Die Temperature	190	°C

Resin Grade	Manufacturer	Category	Trademark
Sumitomo Phenolic FM 4005X4649	Sumitomo Bakelite North America, Inc.	Phenolic	Sumitomo Phenolic
Advanced-PP 1128N	Advanced Petrochemical Company	PP Homopolymer	Advanced-PP
ESENTTIA 40H92	Polipropileno del Caribe S.A.	PP Homopolymer	ESENTTIA
Karina GRAY PVC COMPOUND -E 813-18/190-Y-RT-PO	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
OXPEKK® IG300	Oxford Performance Materials, Inc.	PEKK	OXPEKK®