MAJORIS FG308X - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ZdAFG_MAJORIS-FG308X---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS FG308X - 8229 is a high performance reinforced polypropylene compound intended for injection moulding. MAJORIS FG308X - 8229 has been developed especially for demanding applications in various engineering sectors. MAJORIS FG308X - 8229 has high rigidity and impact strength, good dimensional stability, very good stiffness and good creep resistancy also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 2.00mm | 1.0 | % | Internal method |
| Flow direction : 2.00mm | 0.30 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8170 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 102 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 7300 | MPa | ISO 178 |
| Flexural Stress | 173 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate | ||
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Screw speed: Low to mediumBack pressure: Low to medium |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130D55 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| TYLON® 8433 | Tyne Plastics LLC. | Nylon 66 | TYLON® |
| Zhongfa PP GR-20H | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Dryflex® A2 600609 | ELASTO | SEBS | Dryflex® |
| KOPLA PA6 KNG1090 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |