SCHULATEC® PEEK WR 30 MV 14
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULATEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0I28rZ_SCHULATEC-PEEK-WR-30-MV-14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| polyetheretherketone, anti-friction/anti-wear with PTFE, graphite and carbon fiber, medium viscosity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 2.4 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 14900 | MPa | ISO 178 |
| Flexural Stress | 218 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 34 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed) | 291 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 360 to 370 | °C | |
| Middle Temperature | 380 to 390 | °C | |
| Front Temperature | 390 to 400 | °C | |
| Nozzle Temperature | 360 to 380 | °C | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 170 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on annealed samples 3,2 mm thick, 200°C/2h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 4240 NAT 01 | Prime PVC® | PVC, Rigid | Prime |
| megol® A 60/A1 | API SpA | SEBS | megol® |
| Texalan® 3 Series 372D | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| ALKAMIX™ MB-6002 | Marplex Australia Pty. Ltd. | Unspecified | ALKAMIX™ |
| Petrothene® YR19548 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |