Generic Nylon 66 - Aramid Fiber
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 057GRd_Generic-Nylon-66---Aramid-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Aramid Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 - 1.27 | g/cm³ | ASTM D792 |
| 23°C | 1.22 - 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.34 - 2.0 | % | ASTM D955 |
| Transverse flow : 23°C | 2.0 - 2.1 | % | ASTM D955 |
| 23°C | 0.95 - 2.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.48 - 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2960 - 9470 | MPa | ASTM D638 |
| 23°C | 3420 - 4170 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 80.7 - 93.0 | MPa | ASTM D638 |
| Fracture, 23°C | 68.9 - 100 | MPa | ISO 527-2 |
| 23°C | 57.9 - 130 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 8.3 | % | ASTM D638 |
| Yield, 23°C | 3.0 - 6.0 | % | ISO 527-2 |
| Fracture, 23°C | 3.9 - 8.2 | % | ASTM D638 |
| Fracture, 23°C | 3.3 - 9.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2700 - 3960 | MPa | ASTM D790 |
| 23°C | 3000 - 3550 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 109 - 143 | MPa | ASTM D790 |
| 23°C | 106 - 120 | MPa | ISO 178 |
| Coefficient of Friction | 0.11 - 0.56 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 4.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 15 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 40 - 140 | J/m | ASTM D256 |
| 23°C | 3.9 - 5.8 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 460 - 760 | J/m | ASTM D256 |
| 23°C | 25 - 49 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 232 - 250 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 239 - 247 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 135 - 247 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 87.6 - 246 | °C | ISO 75-2/A |
| Continuous Use Temperature | 109 - 121 | °C | ASTM D794 |
| Vicat Softening Temperature | 200 - 260 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 3.5E-5 - 6.7E-5 | cm/cm/°C | ASTM D696 |
| Flow | 6.7E-5 - 7.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral | 8.1E-5 - 9.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 8.3E-5 - 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 9.8E+12 - 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+2 - 7.5E+15 | ohms·cm | ASTM D257 |
| Insulation Resistance (23°C) | 9.8E+11 - 1.0E+12 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 105 | °C | |
| Drying Time | 3.8 - 11 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 271 - 300 | °C | |
| Middle Temperature | 281 - 300 | °C | |
| Front Temperature | 281 - 301 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 282 - 290 | °C | |
| Mold Temperature | 86.3 - 105 | °C | |
| Injection Pressure | 96.5 - 110 | MPa | |
| Back Pressure | 0.254 - 0.262 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Aramid FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilene F8100GF20-03 | API Polymers, Inc. | PP Homopolymer | Michilene |
| Monprene® MP-1442A | Teknor Apex Company | TPE | Monprene® |
| ExxonMobil™ LDPE LD 313.NF | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Fiberfil® J-60/20/E8 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Sylvin 8999-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |