China PPS hFR52
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zzhimQ_China-PPS-hFR52.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS-hFR52 is filled PPS compound, which is filled with mineral based on the PPS resin. It shows high rigidity, creep resistance, high-temperature resistance, inherent flame resistance, chemical resistance, excellent electrical insulation properties, arc resistance, low water absorption, easy processing, low mold shrinkage, good dimensional stability, and radiation resistance. Its colour is offwhite. Owing to its high performance and light colour, it's an excellent selection for outer decorating parts with high temperature resistance in electronic, electric and medical industry. Such as: outer shells of electric appliances, salvers, high-temperature disinfecting instruments, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | Internal method |
| Molding Shrinkage - Flow | 0.25 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 109 | MPa | Internal method |
| Tensile Elongation (Break) | 1.7 | % | Internal method |
| Flexural Modulus | 15500 | MPa | Internal method |
| Flexural Strength | 175 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 7.0 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 267 | °C | Internal method |
| Melting Temperature | 282 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.3E+15 | ohms | Internal method |
| Volume Resistivity | 1.0E+17 | ohms·cm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 4 to 8hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultra Purge P-O | Moulds Plus International USA, Inc. | Proprietary | Ultra Purge |
| Grivory® GV-5HL black 9914 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Kepital® F10-03H LOF | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| KYDEX® XDWG | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| LOXIM 830 12 HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |