FORMULA P ELAN XP 515
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zz6xtw_FORMULA-P-ELAN-XP-515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene reinforced with nano-clay. This material has very good scratch-resistance and good impact-strength. Due to high MFI it is easy to mold. This type is designed for automotive interior/exterior trim. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 | MPa | ISO 527-2 |
| Fracture | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 100 | % | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 49.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180 | ||
| -20°C | 4.5 | kJ/m² | ISO 180 |
| 23°C | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 60.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 20 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 240 - 255 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SA861 | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| Topolymer® 6200-T/C/A | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Wanthane® WHT-1564 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| MAJORIS DFR330 - 8487 | AD majoris | PP, Unspecified | MAJORIS |
| Polaris™ C 80355-13 | Ashland Performance Materials | Polyester, TS | Polaris™ |