Bormod™ HD915CF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zyfGgY_Bormod-HD915CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormod HD915CF is a high cristallinity homopolymer film resin, based on special Borstar nucleating technology. This grade is specifically designed to be extruded as stiff core layer with a copolymer coat layer of Borclear RE718CF. This grade is suitable for the manufacturing of unoriented films for metallisation. Optical properties will not be deteriorated as with conventional homo or copolymers at these temperatures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 to 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C, Injection Molded) | 2100 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.30 to 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Force (50 µm) | 1.90 | N | ISO 7765-2 |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 1600 to 1800 | MPa | |
| TD : 50 µm | 1600 to 1800 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 35.0 to 55.0 | MPa | |
| TD : 50 µm | 30.0 to 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 80 to 120 | % | |
| TD : Break, 50 µm | 80 to 120 | % | |
| Instrumented Dart Impact (50 µm, Total Energy) | 800 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 158 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 164 to 170 | °C | ISO 3146 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 90 | ASTM D2457 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNIACE® H-270 | Nippon A&L Inc. | PC+ABS | TECHNIACE® |
| TYNELOY® CE4200 | Tyne Plastics LLC. | PC+PET | TYNELOY® |
| NANTEX® 630A | Nantex Industry Co., Ltd. | NBR | NANTEX® |
| Delrin® 100TL NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Sylvin 8353-98FUV White 1513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |