Di-Pak™ R-4354
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zxbeZu_Di-Pak-R-4354.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4354 A 100% solids, room temperature cure, dielectric insulating material used for sealing, coating, bonding and potting. R-4354 is a medium viscosity, slightly thixotropic system. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.050 to 0.15 | % | ASTM D2566 |
| Weight - per cubic inch | 18 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 80 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 40.0 to 60.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2460 | MPa | ASTM D638 |
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.4E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.40 | ||
| 100 kHz | 3.10 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.018 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 96, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity 2(25°C) | 9500 | cP | ASTM D4878 |
| Demold Time (21°C) | 720 to 1100 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Range: 7000 to 12000 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 126218 B | RTP Company | PLA | RTP |
| XAREC™ EA 537 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| Badamid® A70 TM-Z1 | Bada AG | Nylon 66 | Badamid® |
| Fainplast PVC PH 75 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| IDI BMC B20 (Glass Content 8%) | IDI Composites International | TS, Unspecified | IDI BMC |