Smooth-On Super Instant®
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Smooth-On |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zx3Toz_Smooth-On-Super-Instant-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Smooth-On Super Instant® Epoxy is a two component, clear amber adhesive designed to provide rapid bonding. When mixed in equal proportions—either by volume or by weight—curing takes place quickly enough to permit handling in 5 to 10 minutes at room temperature. Super Instant® adheres to metals such as steel, aluminum and brass, to wood, glass, masonry and many hard plastics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Viscosity | Light-paste |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 60 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 186 | MPa | ASTM D638 |
| Tensile Strength | 7.58 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Compressive Modulus | 793 | MPa | ASTM D695 |
| Compressive Strength | 31.0 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life (23°C) | 2.5 | min | |
| Demold Time (23°C) | 10 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PH200NS | Premier Polymers, LLC. | PP Homopolymer | Premier |
| RELENE® S42005 | Reliance Industries Limited | HDPE | RELENE® |
| NEFTEKHIM PP 1525H (S28F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| CYCOLAC™ MG38N resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Politer TF2 | Poliblend S.p.a. | PBT | Politer |