Lucon® CP6054
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zwwx3D_LuconCP6054.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Electrostatic Dissipation (1.0E+04 ~ 1.0E+06 ohm) Application LCD Cell Tray |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 8.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 5000 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 1.0E+6 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 300 - 330 | °C | |
| Nozzle Temperature | 300 - 330 | °C | |
| Processing (Melt) Temp | 300 - 330 | °C | |
| Mold Temperature | 90 - 120 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKAEXCEL® PES 4100G | Sumitomo Chemical Co., Ltd. | PESU | SUMIKAEXCEL® PES |
| Mowiflex™ FX 407 | Kuraray Co., Ltd. | PVOH | Mowiflex™ |
| UBESTA 3030 JFX3 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| NYCOA Polyamide 5400 | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| HiFill® TPU/E 0140 | Techmer Engineered Solutions | TPU, Unspecified | HiFill® |