Starflam B28UL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zwd9S4_Starflam-B28UL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam B28UL is Unfilled Halogen Free and Red Phosphorous Free Flame Retardant Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.2 to 1.6 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.6 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 80.0 | MPa | |
| Break | 80.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.9 | % | |
| Break | 4.5 | % | |
| Flexural Modulus 2 | 3000 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -40°C | 3.0 | kJ/m² | |
| -30°C | 4.0 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 180 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 68.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 202 | °C | ISO 306/B50 |
| -- | 200 | °C | ISO 306/B120 |
| Ball Pressure Test 7(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.29 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 100 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.10 | ||
| 60 Hz | 3.10 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 8.7E-3 | ||
| 60 Hz | 8.7E-3 | ||
| 1 MHz | 0.018 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 600 | V | |
| Solution B | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 250 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 |
| 7 . | 125°C ±2°C |
| 8 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4LEX® 10F23100 | 4Plas | PC | 4LEX® |
| Chiao Fu PA66 MD212LB30 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Ebalta GM 973 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Halene P B202S | Haldia Petrochemicals Ltd. | PP Random Copolymer | Halene P |
| Okirol® E-5F | DIOKI d.d. | PS (EPS) | Okirol® |