Diakon® CRG873
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zwaior_Diakon-CRG873.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon® CRG873 is a Polymethyl Methacrylate Acrylic material. It is available in Europe for injection molding. Important attributes of Diakon® CRG873 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 5.7 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.35 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 44 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 58 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 5.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ISO 306/A |
| -- | 85.0 | °C | ISO 306/B |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 250 | °C | |
| Middle Temperature | 200 to 270 | °C | |
| Front Temperature | 210 to 280 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® FEP 9835 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| SWANCOR Epoxy 917 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Vi-Chem PVC VNC95-80I | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| ELASTOSIL® LR 3003/85 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Honeywell PCTFE P5000HS | Honeywell | PCTFE | Honeywell PCTFE |