Retpol® 1024/5 HS UV2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zw9G63_Retpol-1024-5-HS-UV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton 1024/5 HS UV2 is a 20% talc filled polypropylene compound. It is a high flow injection moulding grade developed for rigid components requiring good mar resistance and high impact strength. It is stabilized to meet automotive heat ageing and weathering requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.1 to 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 90 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 74 | ||
| Shore D, 15 sec, 3.00 mm | 66 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 43 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 42 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 116 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic ET 6235Z | 3M Advanced Materials Division | ETFE | 3M™ Dyneon™ Fluoroplastic |
| Gallonprene® GP520-8009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Epoxies, Ect. 20-2390 | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| Karina RED PVC COMPOUND 835-42/14-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8250-70 Brown 7460 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |