CYCOLOY™ CE3510 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zw80xG_CYCOLOY-CE3510-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact, high heat and excellent extrusion and thermoforming characteristics. Halogen free according to DIN VDE 0472/815 for cable channels |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2680 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break 3 | 49.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.3 | % | ASTM D638 |
| Yield | 4.6 | % | ISO 527-2/50 |
| Break 5 | 35 | % | ASTM D638 |
| Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2610 | MPa | ASTM D790 |
| -- 7 | 2480 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 14 14 | kJ/m² | |
| 23°C | 45 45 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break No Break | ||
| 23°C | No Break No Break | ||
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 660 | J/m | ASTM D256 |
| -30°C 11 | 12 | kJ/m² | ISO 180/1A |
| 0°C 12 | 14 | kJ/m² | ISO 180/1A |
| 23°C 13 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 14 | ISO 180/1U | ||
| -30°C | No Break No Break | ||
| 23°C | No Break No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 111 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 15 | 111 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 16 | 100 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 116 | °C | ISO 306/B50 |
| -- | 118 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 44 | kV/mm | |
| 1.60 mm, in Oil | 27 | kV/mm | |
| 3.20 mm, in Oil | 18 | kV/mm | |
| Comparative Tracking Index (CTI) | PLC 3 PLC 3 | UL 746 | |
| Comparative Tracking Index | 225 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | |
| 1.50 mm | 825 | °C | |
| 3.00 mm | 825 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Cylinder Zone 1 Temp. | 235 to 260 | °C | |
| Cylinder Zone 2 Temp. | 240 to 265 | °C | |
| Cylinder Zone 3 Temp. | 245 to 270 | °C | |
| Cylinder Zone 4 Temp. | 245 to 270 | °C | |
| Adapter Temperature | 245 to 270 | °C | |
| Melt Temperature | 230 to 270 | °C | |
| Die Temperature | 235 to 260 | °C | |
| Calibration Temp, First | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 120*10*4 mm |
| 16 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP340M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| TRIBOFORCE® PA66 C0200 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | TRIBOFORCE® |
| Nipoflex® 750 | TOSOH Corporation | EVA | Nipoflex® |
| Edgetek™ X ET3300-8031 NHFR NC001 | PolyOne Corporation | PBT | Edgetek™ |
| LEXAN™ HFD1830 resin | SABIC Innovative Plastics | PC | LEXAN™ |