Beetle® PBTS800
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Beetle® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zvUE0r_Beetle-PBTS800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBTC115F is a reinforced PBT/PET alloy containing 15% glass fiber. It achieves the best balance of mechanical properties and heat resistance, with excellent surface finish and mold release. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.6 - 2.6 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain 2 | 84.0 | MPa | ISO 178 |
| -- 3 | 99.0 | MPa | ISO 178 |
| Flexural Strain at Break | 6.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | Internal method | |
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | < 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| 背压：低注射压力：高 |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions. The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | Conventional deflection |
| 3 . | Yield strength |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Plus HDPE 5502 | ResMart | HDPE | ResMart Plus |
| NYLOY® KF-0010N 2140B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| APEX® 89-P334-C | Teknor Apex Company | PVC, Flexible | APEX® |
| Iupital® F40-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| POCAN® KU 2-7604 000000 | LANXESS Corporation | PC+PBT | POCAN® |