MAJORIS AFR067 - 8487
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zvKE6m_MAJORIS-AFR067---8487.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AFR 067 - 8487 is a halogen free flame retardant compound UL 94 V2, intended for extrusion and profiles. The product is available in natural but other colours can be provided on request AFR 067 - 8487 produce very low level of toxicity and low smoke density in the case of a fire. This product is UV stabilised. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.6 to 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 18.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Ball Pressure Test (125°C) | Pass | NF C 61-303 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 850 | °C | IEC 60695-2-12 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 190 | °C | |
| Cylinder Zone 3 Temp. | 180 to 190 | °C | |
| Cylinder Zone 5 Temp. | 180 to 190 | °C | |
| Melt Temperature | 200 | °C | |
| Head Temperature | 200 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravaflex BR H CIS | Ravago Group | PBR, High Cis | Ravaflex |
| BCC Resins BC 8001 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| K-Bin Rigid PVC KB-7400 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |
| LONGLITE® PBT 3020-104S | CCP Group | PBT | LONGLITE® PBT |
| Optix® CP-61 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |