DOMAMID® A1-023-V30-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zvDhA6_DOMAMID-A1-023-V30-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, medium viscosity, 30% glass fiber reinforced, natural - rapid solidification |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 45.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 1.0 | % | |
| Flow : 23°C, 72 hr | 0.30 | % | |
| Water Absorption 2 | ISO 62 | ||
| Saturation, 23°C | 1.7 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 30 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 217 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 181 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 3 | 7250 | MPa | ISO 178 |
| Flexural Stress 4 | 270 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 217 | °C | ISO 306/A50 |
| -- | 214 | °C | ISO 306/B50 |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | VDE 0303-3 |
| Volume Resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(2.00 mm) | 40 | mm/min | ISO 3795 |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | VDE 0471/2 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 24 hrs |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecopet® PT74 CR20 BK111 PR | Eurotec Engineering Plastics | PET | Tecopet® |
| DINALON® A1S25 G35 (Glass) | Grupo Repol | Nylon 66 | DINALON® |
| Geon™ Vinyl Packaging RB-FG | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| Hanwha Total PP TB52T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| GELOY™ EXGY0058 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |