LNP™ LUBRICOMP™ WG003 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zvDZPI_LNP-LUBRICOMP-WG003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP WG003 is a compound based on Polybutylene Terephalate resin cantain Graphite. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.7 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3200 | MPa | ISO 178 |
| Flexural Stress | 83.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 179 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 71.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 9.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SMG7500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| SKYBOND® 6000 | Industrial Summit Technology Co. | API | SKYBOND® |
| Formolene® 4143T | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Petrothene® YR92866 | LyondellBasell Industries | LDPE+EVA | Petrothene® |
| Sylvin 9812-80C White 1458 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |