Stanyl® TW271B3
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zv3359_Stanyl-TW271B3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stanyl® TW271B3 is a Polyamide 46 (Nylon 46) material filled with 15% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary attribute of Stanyl® TW271B3: Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 12500 | 6700 | MPa | |
| 120°C | 6300 | -- | MPa | |
| 160°C | 5700 | -- | MPa | |
| 180°C | 5400 | -- | MPa | |
| 200°C | 5100 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 185 | 120 | MPa | |
| Break, 120°C | 108 | -- | MPa | |
| Break, 160°C | 92.0 | -- | MPa | |
| Break, 180°C | 84.0 | -- | MPa | |
| Break, 200°C | 76.0 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 2.0 | 5.0 | % | |
| Break, 120°C | 5.0 | -- | % | |
| Break, 160°C | 5.0 | -- | % | |
| Break, 180°C | 5.0 | -- | % | |
| Break, 200°C | 5.0 | -- | % | |
| Flexural Modulus | 11000 | 5800 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 6.0 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+3 | -- | ohms·cm | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7600 UV | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Texalan® 2 Series 295A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 2 Series |
| Xuchuan XCS-2067T | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| AMTOPP IM20 | Inteplast Group | PP, Unspecified | AMTOPP |
| LNP™ THERMOCOMP™ JF004E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |