Order Products : sales@su-jiao.com
SABIC® PP PHC26
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ztRR17_SABIC-PP-PHC26.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines very high impact resistance, also at low temperatures, with high stiffness and offers good flow properties. Due to its narrow molecular weight distribution, the very low tendency to warp and the excellent surface quality, SABIC® PP PHC26 is typically used in injection moulding of suitcase shells, crates & boxes and automotive parts. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 | |
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1300 | MPa | ASTM D638 |
| -- | 1250 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 22.0 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 9.0 | kJ/m² | |
| 0°C | 15 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 110 | J/m | ASTM D256A |
| 0°C | 200 | J/m | ASTM D256A |
| 23°C | No Break | ASTM D256A, ISO 180/1A | |
| -20°C | 10 | kJ/m² | ISO 180/1A |
| 0°C | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 50.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 68.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P40B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Tenac™ Z3010 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| ALKAMIX™ MB-UHSMB | Marplex Australia Pty. Ltd. | LDPE | ALKAMIX™ |
| GLAMIDE® TY-791HT | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| Sylvin 9077-90LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |