SUPREME Specialty PS SP6520
| Category: | PS (Specialty) , Specialty Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ztMSwU_SUPREME-Specialty-PS-SP6520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUPREME Specialty PS SP6520 is a special polystyrene product,. It can be processed by extrusion, thermoforming or injection molding, and is available in North America, Africa and the Middle East, Europe or the Asia-Pacific region. The application fields of SUPREME Specialty PS SP6520 include houses and disks/racks. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 1500 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 44.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 | ohms | ASTM D257 |
| Volume Resistivity (23°C, 3.20 mm) | 1.0E+9 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257, 3.2 mm, 23°C, injection molded: 1E9 to 1E10 ohmsVolume Resistivity, ASTM D257, 23°C, 3.2 mm, injection molded: 1E9 to 1E10 ohm-cmStatic Charge Decay, MIL-PRF-81705D: <2 sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | < 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | < 230 | °C |
| Extrusion instructions |
|---|
| Mold Temp: 40 to 60°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 K | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Therma-Tech™ X TT6000-8711 EI NHFR WHITE | PolyOne Corporation | Nylon 6 | Therma-Tech™ |
| Vi-Chem PVC V221-80I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Toyolac® A25C-300 | Toray Resin Company | AS | Toyolac® |
| NYCOA Polyamide 5013 HS | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |