Rynite® FR515 NC010
| Category: | PET , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Rynite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zt2m5H_Rynite-FR515-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced, Flame Retardant, Polyethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow 1 | 1.2 | % | |
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % | |
| Flow 2 | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 88 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 107 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 5940 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 7.0 | kJ/m² | |
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 20 | kJ/m² | |
| -30°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Melting Temperature 3 | 254 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | 3.3E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | 1.2E-5 | cm/cm/°C | |
| Transverse | 8.8E-5 | cm/cm/°C | |
| Transverse : -40 to 23°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.10 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| 100 Hz | 3.70 | IEC 60250 | |
| 1 MHz | 3.70 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 4.0E-7 | ASTM D150 | |
| 1 MHz | 1.5E-6 | ASTM D150 | |
| 100 Hz | 9.0E-3 | IEC 60250 | |
| 1 MHz | 0.015 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.860 mm | V-0 | ||
| 1.50 mm | V-0 5VA | ||
| Oxygen Index | 32 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Annealed |
| 2 . | Annealed |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sorta Clear® 18 | Smooth-On, Inc | Silicone | Sorta Clear® |
| BB-AMIDE 5011 | BB Resins S.r.l. | Nylon, Unspecified | BB-AMIDE |
| Cosmic Epoxy CP7311 | Cosmic Plastics, Inc. | Epoxy | Cosmic Epoxy |
| Exelene® HDPE PE80 | Montachem International, Inc. | HDPE, HMW | Exelene® HDPE |
| Elastollan® R 6000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |