Order Products : sales@su-jiao.com
Generic Nylon 6 Alloy
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zsw8Bo_Generic-Nylon-6-Alloy.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 Alloy This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 - 1.14 | g/cm³ | ASTM D792 |
| -- | 1040 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate | 1.34 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (23°C) | 0.80 - 1.2 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 1.5 | % | ASTM D570 |
| Saturation | 4.8 | % | ISO 62 3 |
| Balance | 1.5 | % | ISO 62 4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 840 | MPa | ISO 527-2 5 |
| Tensile Stress | |||
| Yield | 40.0 | MPa | ISO 527-2 6 |
| Fracture, 23°C | 74.8 - 85.8 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield | 5.5 | % | ISO 527-2 7 |
| Fracture, 23°C | 10 - 84 | % | ASTM D638 |
| Tensile Creep Modulus | ISO 899-1 8 | ||
| 1 hr | 1290 | MPa | ISO 899-1 |
| 1000 hr | 601 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 2650 - 3030 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 101 - 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 - 82 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 55.0 - 65.1 | °C | ASTM D648 |
| Melting Temperature | |||
| -- | 215 - 220 | °C | |
| -- 9 | 220 | °C | ISO 11357-3 10 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric strength | 37 | kV/mm | IEC 60243-1 11 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 81.7 - 82.2 | °C | |
| Drying Time | 4.0 - 4.1 | hr | |
| Mold Temperature | 71.0 - 72.1 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 AlloyThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | 10 °C/min |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S HS 105 M NAT | Radici Plastics | Nylon 6 | Radilon® |
| Stratasys ABS-M30i | Stratasys | ABS | Stratasys |
| APEX® 88-N131M-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ELASTOSIL® LR 3070/20 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Wuxi Jiahong EB-209 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |