LNP™ THERMOCOMP™ GF003 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zs6gIQ_LNP-THERMOCOMP-GF003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* GF003 is a compound based on Polysulfone resin containing 15% Glass Fiber. Also known as: LNP* Thermocomp* Compound GF-1003 Product reorder name: GF003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.34 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5490 | MPa | ASTM D638 |
| -- | 5430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 86.0 | MPa | ASTM D638 |
| Break | 86.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 2.9 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Break 4 | 3.1 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 4720 | MPa | ASTM D790 |
| -- 6 | 4710 | MPa | ISO 178 |
| Flexural Strength 7(Break, 50.0 mm Span) | 146 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 45 | J/m | ASTM D256 |
| 23°C 8 | 4.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 9 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 14.6 | J | ASTM D3763 |
| -- | 3.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 184 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 185 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 178 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 179 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6048EB | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| VAMPAMID HT 0024 V0 | Vamp Tech | PPA | VAMPAMID |
| Halar® 2408DA | Solvay Specialty Polymers | ECTFE | Halar® |
| Kotex KV-20FD | Kotec Corporation | PC | Kotex |
| POLYFLAM® RPP 2000 E | A. Schulman Europe | PP Homopolymer | POLYFLAM® |