Staramide RFB53U
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zqamNI_Staramide-RFB53U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide RFB53U is Glass Bead and Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 1525 VK Z4) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.70 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 131 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7500 | MPa | ISO 178 |
| Flexural Stress | 201 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 253 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 229 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 275 to 285 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 623B | SABIC Americas, Inc. | PP Random Copolymer | SABIC® PP |
| Ferro PP TPP40AA03WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| HiPrene® MR71SE | GS Caltex | PP, Unspecified | HiPrene® |
| LUVOCOM® 1105-8320 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Sylvin 8225-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |