Solef® 60512/0550 and 60512/0150
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zqAwDx_Solef-60512-0550-and-60512-0150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 60512/0550 and Solef® 60512/0150 are PVDF grades compounded with PTFE for extrusion of anti-wear tapes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 to 1.82 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 2.0 to 4.5 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 1.50 mm) | 1100 to 1350 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 1.50 mm | 30.0 to 40.0 | MPa | |
| Break, 23°C, 1.50 mm | 30.0 to 40.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 1.50 mm | 8.0 to 12 | % | |
| Break, 23°C, 1.50 mm | 50 to 300 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.10 to 0.20 | ||
| vs. Itself - Static | 0.050 to 0.20 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 5.00 to 10.0 | mg | ASTM D4060 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 170 to 174 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 144 to 148 | °C | ASTM D3418 |
| Crystallization Heat | 38.0 to 48.0 | J/g | ASTM D3417 |
| Heat of Fusion - (80°C to end of melting) | 41.0 to 50.0 | J/g | ASTM D3417 |
| Note Message | |
|---|---|
| 1 . | Type V, 1.0 mm/min |
| 2 . | Type V, 50 mm/min |
| 3 . | Type V, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styropor® F 315 E | BASF Corporation | PS (EPS) | Styropor® |
| Ultramid® B3EG7 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| Bergamid™ A70 G50 H Natural | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Geon™ Vinyl Rigid Extrusion 87358 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Plasmer 1070N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |