SCANTEC PC S60R GF10 V0
| Category: | PC , Polycarbonate |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANTEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zq97i1_SCANTEC-PC-S60R-GF10-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced Flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.60 | % | |
| Flow | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3500 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 131 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 383 | RTP Company | PC | RTP |
| Miraprene® QS1624D | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| Elastron® V P.V101.A45.N | Elastron USA, Inc. | TPV | Elastron® V |
| EPO-TEK® 323LP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostacom X M2 U38 | LyondellBasell Industries | PP Copolymer | Hostacom |