NORYL™ SE100HX resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zpBDMH_NORYL-SE100HX-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Improved productivity and reliability. Nonchlorinated, nonbrominated FR. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow 1 | 0.50 to 0.70 | % | |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 61.4 | MPa | |
| Break | 46.9 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.5 | % | |
| Break | 21 | % | |
| Flexural Modulus 4(100 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 89.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 91 | J/m | |
| 23°C | 230 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 3.28 | J | |
| 23°C, Energy at Peak Load | 31.6 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 94.4 | °C | |
| RTI Elec | 95.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 95.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | ||
| 5.99 mm | V-0 | ||
| Radiant Panel Listing (UL) | YES |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 216 to 266 | °C | |
| Middle Temperature | 227 to 271 | °C | |
| Front Temperature | 238 to 277 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 54.4 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-88UV Clear 8418 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ HU1110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| KOPLA PP KPG1040 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| ExxonMobil™ PP7654KNE2 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Sylvin 8260-80 White 1439 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |