Niplene T20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niplene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zo4Coy_Niplene-T20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, talc filled at 20%, suitable for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3 | 2800 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® TC502 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| ALCOM® PC 740/4 UV WT1082-08LD2 | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| ChronoThane™ P 55D | AdvanSource Biomaterials Corp. | TPU-Polyether | ChronoThane™ |
| EVERLON® TY-60 | Ever Polymer Co., Ltd. | SBS | EVERLON® |
| KOPA® KN133G15HS | Kolon Plastics, Inc. | Nylon 6 | KOPA® |