Latiblend 6252 H2 G/30
| Category: | Nylon+PP , Polyamide + PP |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | znkS9C_Latiblend-6252-H2-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6)/Polypropylene homopolymer (PPh). Heat stabilised. Glass fibres. Product UL certified. Good thermal resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 to 1.1 | % | |
| Flow : 2.00 mm | 0.35 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 9400 | MPa | |
| 60°C | 6400 | MPa | |
| 90°C | 4700 | MPa | |
| 120°C | 3100 | MPa | |
| 150°C | 2100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 80.0 | MPa | |
| Yield, 90°C | 55.0 | MPa | |
| Yield, 120°C | 40.0 | MPa | |
| Yield, 150°C | 30.0 | MPa | |
| Break, 23°C | 125 | MPa | |
| Break, 60°C | 80.0 | MPa | |
| Break, 90°C | 55.0 | MPa | |
| Break, 120°C | 40.0 | MPa | |
| Break, 150°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 4.0 | % | |
| Yield, 90°C | 5.0 | % | |
| Yield, 120°C | 6.0 | % | |
| Yield, 150°C | 7.0 | % | |
| Break, 23°C | 2.7 | % | |
| Break, 60°C | 4.6 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 7.0 | % | |
| Break, 150°C | 8.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 55 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 195 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 170 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® SB9430 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| SIMONA® PP-C | SIMONA AMERICA, Inc. | PP Copolymer | SIMONA® |
| Elastron® D D300.A90.B | Elastron USA, Inc. | SBS | Elastron® D |
| ICORENE® 1869 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| TechnoFiber PP LGF 20-10-01 HI | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |