Nylene® 409

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zneW3c_Nylene-409.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Heat stabilized version of 406 which is a general purpose, fast cycling molding resin

Crystallization initiators provide fast molding cycles through rapid melt set-up. In addition to protection from heat degradation

Parts molded from 409 have better dimensional stability at moisture equilibrium than parts molded from conventional nylon

Optimum processing conditions should provide a melt temperature of 450°F-470°F at the nozzle

General Information
Additive	Heat Stabilizer
Features	Fast Molding Cycle General Purpose Good Dimensional Stability Heat Stabilized
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.13	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.90	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	75.2	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	25	%	ASTM D638
Flexural Modulus (23°C)	2760	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	43	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	182	°C
1.8 MPa, Unannealed	71.1	°C
Peak Melting Temperature	216	°C	ASTM D3418

Flammability	Nominal Value		Test Method
Flame Rating (1.47 mm)	V-2		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	232 to 243	°C

Resin Grade	Manufacturer	Category	Trademark
SCANTEC PC S60R GF30 V0	Polykemi AB	PC	SCANTEC
TEKNIFLEX® PXA 1280	Tekni-Films, a div of Tekni-Plex	Film, Copolyester/PCTFE	TEKNIFLEX®
Ferro PP LPP20BN44HB ALMOND	Ferro Corporation	PP Copolymer	Ferro PP
Edistir® N 1840	Versalis S.p.A.	PS (GPPS)	Edistir®
Karina CLEAR CRYSTAL PVC COMP. -E 85/201-DA-IS-SI-AT	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina