HONES® PPS HS-B7-2
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Guangdong Shunde Hones Polymer Material Co., Ltd. |
| Trademark: | HONES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | znK3QI_HONES-PPS-HS-B7-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low warpage, Good appearance |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 0.22 | % | |
| Across Flow : 2.00 mm | 0.45 | % | |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 120 | MPa | Internal Method |
| Tensile Elongation (Break) | 1.2 | % | Internal Method |
| Flexural Modulus | 9500 | MPa | Internal Method |
| Flexural Strength | 220 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | Internal Method |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 3.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (3.00 mm) | 20 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 1 kHz | 5.20 | ||
| 1 MHz | 5.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 kHz | 2.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (310°C) | 200 | Pa·s | ISO 11443 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAJORIS UG407 - 8229 | AD majoris | Nylon 66 | MAJORIS |
| Pro-fax SV258 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| PRL PC/TP-FR3 | Polymer Resources Ltd. | PC+Polyester | PRL |
| Nypol® PA A3 G30 N10 NTLA010 NR314 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Lucky Enpla LPC1003 | Lucky Enpla Co LTD | PC | Lucky Enpla |