Halene L 71501S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zn4Giw_Halene-L-71501S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
71501S is a LLDPE blown film grade produced by the Spherilene Technology. This grade can be used in General Purpose Packaging Film Applications. 71501S is additivated with slip and antiblocking additives for excellent openability and slip properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 16.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 650 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 750 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 150 | g | ASTM D1922 |
| TD : 25 µm, blown film | 400 | g | ASTM D1922 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°, 25.0 µm, Blown Film) | 76 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 200 | °C | |
| Cylinder Zone 3 Temp. | 180 - 200 | °C | |
| Cylinder Zone 4 Temp. | 180 - 200 | °C | |
| Cylinder Zone 5 Temp. | 180 - 200 | °C | |
| Melt Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2.0 to 3.0Die Gap: 2.0 to 2.5 mm |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 38 mm Dart, 66 cm Height |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP7210 | Spartech Polycom | PP Copolymer | Spartech |
| VESTAMID® L X7167 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Nypol® PA A3 T30 PRTA010 NR380 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Boda BDF631P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| NORYL™ PX9406P resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |